Kimya ABS-EC Filament - 500 grams
The Kimya ABS-EC 3D filament belongs to the styrenic polymer family. Acrylonitrile Butadiene Styrene electrical conductor (ABS-EC) is a combination of ABS and electrically active additives: carbon nanotubes. ABS-EC is resistant to impact, heat and ageing. It is used in the automotive and electronics industries. The Kimya ABS-EC 3D filament has the following properties:
- Good resistance to impact
- High temperature resistance
- Electrical conductivity
- Complies with the REACH standard
- Product Dimensions: 20.7 × 20.5 × 6 cm; 0.8 kg
FILAMENT PROPERTIES
PROPERTIES |
TEST METHODS |
VALUES |
Diameter |
INS-6713 |
1.75 ± 0.05 mm 2.85 ± 0.05 mm |
Density |
ISO 1183-1 |
1.035 g/cm3 |
Moisture rate |
INS-6711 |
< 0.5 % |
Melt flow index (MFI) |
ISO 1133-1 (@260°c – 10 kg) |
8 - 16 g/10min |
Glass transition temperature (Tg) |
ISO 11357-1 DSC (10°C/min - 20-300°C) |
108 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
PRINTING DIRECTION |
XY |
Printing Speed |
20-60 mm/s |
Infill |
100% - rectilinear |
Infill Angle |
45°/-45° |
Nozzle Temperature |
260-280°C |
Bed T° |
90-110°C |
PRINTED SPECIMENS PROPERTIES
|
PROPERTIES |
TEST METHODS |
VALUES |
ELECTRICAL PROPERTIES |
Surface resistivity |
ASTM D257 |
< 106 Ohms/m² |
MECHANICAL PROPERTIES |
Tensile modulus |
ISO 527-2/5A/50 |
2,398 MPa |
Tensile Strength |
ISO 527-2/1A/50 |
36.7 MPa |
Tensile strain at strength |
ISO 527-2/1A/50 |
2 % |
Tensile Stress at Break |
ISO 527-2/5A/50 |
29.2 MPa |
Tensile strain at break |
ISO 527-2/5A/50 |
5 % |
Flexural modulus |
ISO 178 |
1,393 MPa |
Flexural stress at conventional deflection (3,5% strain)* |
ISO 178 |
49.3 MPa |
Charpy impact resistance |
ISO 179-1/1eA |
27 kJ/m² |
Shore Hardness |
ISO 868 |
67,2 |
Note 1 |
*According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
Note 2 |
The data should be considered as indicative values - Properties can be influenced by production conditions. |